Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC SI-3109G K2007 BK Samsung Cheil South Korea
INFINO®
Electronic and electrical、Automotive components、Electronic and electric p
Carbon fiber flame retard、UV resistance、 High gloss、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.9 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 120 |
| R级 | ASTM D785 | 89 |
| Basic performance | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| melt mass-flow rate | 200℃ 5kg | ASTM D-1238 | 21.0 g/10min |
| Water absorption rate | 24hrimmersion | ASTM D-570 | 0.15 % |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| bending strength | 2.8mm/min | ASTM D-790 | 1100 Kgf/cm |
| ASTM D790 | 88.3 Mpa | ||
| tensile strength | 断裂 | ASTM D638 | 47.1 Mpa |
| Flexural modulus | ASTM D790 | 2450 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 46.0 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| Tensile modulus | ASTM D638 | 2160 Mpa | |
| elongation | 断裂 | ASTM D638 | 47 % |
| tensile strength | 5mm/min | ASTM D-638 | 570 Kgf/cm |
| Tensile modulus | ISO 527-2/50 | 2400 Mpa | |
| bending strength | ISO 178 | 88.0 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| 2.8mm/min | ASTM D-790 | 29000 Kgf/cm | |
| tensile strength | 屈服 | ASTM D638 | 55.9 Mpa |
| Rockwell hardness | ASTM D-785 | 89 R-Scale | |
| Tensile strain | 断裂 | ISO 527-2/50 | 15 % |
| Impact strength of cantilever beam gap | 1/8" | ASTM D-256 | 9 Kgf.cm/cm |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 19 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.30-0.50 % |
| ash content | ISO 3451 | 9.8 % | |
| Shrinkage rate | ASTM D-955 | 0.3-0.5 % | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/SI-3109G K2007 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 127 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 131 °C | |
| vicat | -- | ISO 306/B120 | 147148 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 140 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 128 °C | |
| 1/4" 18.56kgf/cm，HDT | ASTM D-648 | 120 °C | |
| vicat | -- | ISO 306/B50 | 145146 °C |
| 5kg | ASTM D-1525 | N/A °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 142 °C |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 140 °C | |
| UL flame retardant rating | UL 94 | 0.8 V-2 |