ABS SD-0150 FWA572 LOTTE KOREA
STAREX®
Decorative components,Electrical appliances,Automotive sector
Impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/SD-0150 FWA572 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| hardness | Test Condition | Test Method | LOTTE KOREA/SD-0150 FWA572 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 113 |
| R级 | ASTM D785 | 109 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/SD-0150 FWA572 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 51.0 Mpa |
| 屈服3 | ASTM D638 | 41.0 Mpa | |
| bending strength | --4 | ASTM D790 | 62.0 Mpa |
| --5 | ISO 178 | 76.0 Mpa | |
| Tensile modulus | ISO 527-2/50 | 2500 Mpa | |
| Flexural modulus | --4 | ASTM D790 | 2100 Mpa |
| --5 | ISO 178 | 2500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 11 % |
| tensile strength | 断裂 | ISO 527-2/50 | 36.0 Mpa |
| physical property | Test Condition | Test Method | LOTTE KOREA/SD-0150 FWA572 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/SD-0150 FWA572 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 101 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 84.0 °C |
| 0.45MPa,退火,4.00mm，HDT | ISO 75-2/B | 101 °C | |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,4.00mm，HDT | ISO 75-2/A | 79.0 °C |
| 0.45MPa,未退火,4.00mm，HDT | ISO 75-2/B | 92.0 °C | |
| 1.8MPa,退火,4.00mm，HDT | ISO 75-2/A | 98.0 °C |