PC/PTFE DCL-4032 FR SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components、Electronic and electrical、Sports equipment
Thermal stability、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4032 FR |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 10 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 34 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 4.29 J | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 11.6 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4032 FR |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 71.0 Mpa |
| elongation | 断裂 | ASTMD638 | 3.1 % |
| Tensile modulus | ISO527-2/1 | 4290 Mpa | |
| Flexural modulus | ASTMD790 | 4350 Mpa | |
| Bending stress | ISO178 | 114 Mpa | |
| tensile strength | 断裂 | ASTMD638 | 73.4 Mpa |
| Flexural modulus | ISO178 | 4170 Mpa | |
| Tensile modulus | ASTMD638 | 4350 Mpa | |
| bending strength | ASTMD790 | 124 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 2.8 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4032 FR |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.18 % |
| Shrinkage rate | MD:24小时 | ISO294-4 | 0.23 % |
| TD:24小时 | ISO294-4 | 0.67 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.11 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4032 FR |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 141 °C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 140 °C |