PC/ABS EXCELLOY CK10G20 Techno Polymer Co, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 13 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 110 J/m |
| hardness | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 109 |
| R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| bending strength | -- | ASTM D790 | 118 MPa |
| Flexural modulus | -- | ISO 178 | 4910 MPa |
| bending strength | -- | ISO 178 | 117 MPa |
| tensile strength | 屈服 | ASTM D638 | 83.4 MPa |
| 屈服 | ISO 527-2 | 76.0 MPa | |
| Flexural modulus | -- | ASTM D790 | 5300 MPa |
| flammability | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| UL flame retardant rating | ALL | UL 94 | HB |
| physical property | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| melt mass-flow rate | 240°C/10.0kg | ISO 1133 | 7.0 g/10min |
| Shrinkage rate | ISO 294-4 | 0.10to0.30 % | |
| density | ISO 1183 | 1.23 g/cm³ |
| Thermal performance | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10G20 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 123 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |