LLDPE ML2202 SINOPEC SHANGHAI
--
Shock-absorbing pads、Packaging bag、film、Agricultural applications、chip
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | SINOPEC SHANGHAI/ML2202 |
|---|---|---|---|
| Hot Tack | 北欧化工 | 2.5 N |
| Basic performance | Test Condition | Test Method | SINOPEC SHANGHAI/ML2202 |
|---|---|---|---|
| melt mass-flow rate | 190℃，2.16kg | ISO 1133 | 0.25 g/10min |
| 190℃，5kg | ISO 1133 | 1.0 g/10min | |
| density | ISO 1183 | 923 kg/m | |
| melt mass-flow rate | 190℃，21.6kg | ISO 1133 | 22 g/10min |
| Mechanical properties | Test Condition | Test Method | SINOPEC SHANGHAI/ML2202 |
|---|---|---|---|
| tear strength | 纵向 | ISO 527-3 | 3 N |
| Tensile modulus | 横向 | ISO 527-3 | 300 Mpa |
| tensile strength | 屈服,横向 | ISO 527-3 | 13 Mpa |
| Dart impact | ISO 7765-1A | 300 g | |
| tensile strength | 纵向 | ISO 527-3 | 50 Mpa |
| 屈服,纵向 | ISO 527-3 | - Mpa | |
| 横向 | ISO 527-3 | 35 Mpa | |
| elongation at break | 纵向 | ISO 527-3 | 600 % |
| tear strength | 横向 | ISO 527-3 | 7 N |
| Resistance to penetration, strength | 北欧化工 | 60 N | |
| Tensile modulus | 纵向 | ISO 527-3 | 250 Mpa |
| Anti penetration, capable of | 北欧化工 | 5 J | |
| elongation at break | 横向 | ISO 527-3 | 900 % |
| physical property | Test Condition | Test Method | SINOPEC SHANGHAI/ML2202 |
|---|---|---|---|
| melting temperature | ISO 3146 | 124 °C | |
| gloss | ISO 2457 | 15 % | |
| Haze ratio | ISO 1003 | 65 % |