Certificates
ABS K-096 DENKA JAPAN
MALECCA
Pharmaceutical packaging、Thermoforming Application
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DENKA JAPAN/K-096 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 114 |
| R级 | ISO2039-2 | 113 |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/K-096 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/50 | 38.0 Mpa |
| 屈服 | ISO527-2/50 | 48.0 Mpa | |
| Tensile modulus | ISO527-2/1 | 2500 Mpa | |
| Flexural modulus | ASTMD790 | 2350 Mpa | |
| Bending stress | ISO178 | 76.0 Mpa | |
| Tensile modulus | ASTMD638 | 42.0 Mpa | |
| Flexural modulus | ISO178 | 2450 Mpa | |
| ASTMD790 | 74.0 Mpa | ||
| Nominal tensile fracture strain | ISO527-2/50 | 29 % |
| flammability | Test Condition | Test Method | DENKA JAPAN/K-096 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | DENKA JAPAN/K-096 |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.40to0.60 % |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/K-096 |
|---|---|---|---|
| vicat | ISO306/B | 110 °C | |
| 1.8MPa,未退火 | ISO75-2/Af | 90.0 °C | |
| Hot deformation temperature 5 | 1.8MPa,Unannealed | ASTMD648 | 100 °C |
| vicat | ASTMD15256 | 110 °C |