PA6 1013G43 MITSUBISHI ENGINEERING JAPAN
Novamid®
Automotive sector、Electronic and Electrical
high strength、High rigidity、Glass fiber reinforcement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G43 |
|---|---|---|---|
| bending strength | D790 | 2500(1380) Kgf/cm | |
| Stretching length | D638 | 4(5) % | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 98(210) J/m |
| Flexural modulus | D790 | 7.84(4.41) GPa | |
| coefficient of friction | D1894 | 0.35 | |
| Impact strength of cantilever beam gap | 1/8寸 | D256 | 14(30) Kgf.cm/cm |
| 1/8寸 | D256 | 140(290) J/m | |
| Taber wear resistance | D1044 | 14 mg/1000cy | |
| Flexural modulus | D790 | 80000(45000) | |
| tensile strength | D638 | 160(100) Mpa | |
| bending strength | D790 | 250(135) Mpa | |
| tensile strength | D638 | 1650(1040) Kgf/cm | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 10(21) Kgf.cm/cm |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G43 |
|---|---|---|---|
| Dielectric loss | 正切 | D150 | 0.02(0.1) |
| arc resistance | ℃ | 130-140 S | |
| dielectric strength | D149 | 15(15) MV/m | |
| dielectric constant | D150 | 35-53(88) Pf/m |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G43 |
|---|---|---|---|
| Rockwell hardness | D785 | 121(113) R | |
| Shrinkage rate | 0.2/0.4 MD% | ||
| Water absorption rate | D570 | 2.5 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G43 |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 220 °C |
| Linear coefficient of thermal expansion | D696 | 3 | |
| UL flame retardant rating | UL 94 | HB |