Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2407 971000 COVESTRO GERMANY
Makrolon®
Industrial applications、Electrical field、Electronic field、Automotive sector、currency、currency
Low viscosity、UV resistance、High mobility、Thermal stability、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 116 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 250 V |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.00 1MHz |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| Dissipation Factor | 23°C | IEC 60250 | 9E-03 1MHz |
| 23°C | IEC 60250 | 5E-04 100HZ | |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| Tensile creep modulus | 1Hr | ISO 899-1 | 2200 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 14 kJ/m² |
| bending strength | 23°C | ISO 178 | 98.0 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 75 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 2350 Mpa |
| Tensile creep modulus | 1000Hr | ISO 899-1 | 1900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| elongation at break | 23°C | ISO 527-2 | >50 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 66.0 Mpa |
| optical performance | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| transmittance | 1000μm | ISO 13468-2 | 89.0 % |
| refractive index | ISO 489 | 1.58 °C |
| Flame retardant performance | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| UL flame retardant rating | UL -94 | V-2 1.50mm | |
| UL -94 | V-2 2.60mm | ||
| UL -94 | HB 2.70mm | ||
| UL -94 | HB 6.00mm | ||
| UL -94 | HB 3.00mm | ||
| UL -94 | V-2 0.75mm |
| physical property | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.30 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.65 % |
| density | ISO 1183 | 1.2 g/cm³ | |
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 19.0 cm3/10min |
| Water absorption rate | (23°C,50RH) | ISO 62 | 0.12 % |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 0.70 % |
| Thermal performance | Test Condition | Test Method | COVESTRO GERMANY/2407 971000 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 124 °C |
| vicat | ISO 306/B50 | 143 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 136 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6.5E-05 cm/cm/°C |