Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA PW-978W TAIWAN CHIMEI
KIBILAC®
--
High heat resistance、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/TAIWAN CHIMEI/PW-978W
density
ASTMD792
g/cm³
1
density
23°C
ISO1183
g/cm³
1
Melt Volume-Flow Rate (MVR)
220°C/10.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
1
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/TAIWAN CHIMEI/PW-978W
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
6
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
tensile strength
屈服
ASTMD638
Mpa
4
tensile strength
屈服
ISO527-2/50
Mpa
4
tensile strength
断裂
ISO527-2/50
Mpa
3
elongation
断裂
ASTMD638
%
5
elongation
断裂
ISO527-2/50
%
2
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
6
bending strength
ISO178
Mpa
6
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
5
Thermal performance
Test Condition
Test Method
Unit
ASA/TAIWAN CHIMEI/PW-978W
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
8
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
1
Hot deformation temperature
Annealed
ASTMD648
°C
1
Hot deformation temperature
Unannealed
ASTMD648
°C
9
vicat softening point
ASTMD15256
°C
1
vicat softening point
--
ISO306/A50
°C
1
vicat softening point
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
9