Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM TR-20 CF2001 JAPAN POLYPLASTIC
DURACON®
Automotive sector、Industrial machinery、Electronic field、Electrical field
High rigidity、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
Charpy Notched Impact Strength23°CISO179/1eA3.0 kJ/m²
hardnessTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
Rockwell hardnessM级ISO2039-275
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
ColorNumberCF2001/CD3501
Mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
Wear factor0.060MPa,0.15m/sec6JISK72187000 10^-8mm³/N·m
Tensile stressISO527-259.0 Mpa
Wear factor0.49MPa,0.30m/sec4JISK7218150 10^-8mm³/N·m
Dynamic2JISK72180.34
Wear factor0.49MPa,0.30m/sec7JISK72188000 10^-8mm³/N·m
Bending stressISO17896.0 Mpa
Tensile modulusISO527-24500 Mpa
与钢-动态3JISK72180.56
Flexural modulusISO1784100 Mpa
Wear factor0.060MPa,0.15m/sec5JISK7218500 10^-8mm³/N·m
Tensile strain断裂ISO527-25.0 %
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
Surface ResistivityIEC600939E+15 ohms
Volume resistivityIEC600932E+14 ohms·cm
dielectric strength3.00mmIEC60243-121 KV/mm
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
UL flame retardant ratingUL94HB
physical property Test ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
melt mass-flow rate190°C/2.16kgISO113321 g/10min
Melt volume flow rate190°C/2.16kgISO113316.0 cm3/10min
Water absorption rate23°C,24hrISO620.50 %
densityISO11831.53 g/cm³
Thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/TR-20 CF2001
1.8MPa,未退火ISO75-2/A125 °C
MD：23到55°C内部方法8E-05 cm/cm/°C
TD：23to55°C内部方法8E-05 cm/cm/°C