Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A 205F SOLVAY FRANCE
TECHNYL®
Thin walled components、Fasteners、Laptop case
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 80 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 5.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| EuropeanRailwaysCertifications | R22 | EN45545-2 | HL2 |
| R23 | EN45545-2 | HL2 |
| Mechanical properties | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 3200 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 50 % |
| bending strength | 23°C | ISO 178 | 120 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 23°C | ISO 178 | 3000 Mpa |
| bending strength | 23°C | ASTM D790 | 125 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/1A | 60.0 Mpa |
| 屈服,23°C | ASTM D638 | 85.0 Mpa | |
| 屈服,23°C | ISO 527-2/1A | 85.0 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 3350 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 25 % |
| Electrical performance | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| relative permittivity | IEC 60250 | 2.90 | |
| Dissipation Factor | IEC 60250 | 0.030 | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 27 KV/mm |
| Surface Resistivity | IEC 60093 | 5E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| 解决方案B | IEC 60112 | PLC 1 |
| flammability | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| UL flame retardant rating | NFF16-101 | F2 | |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-2 |
| 0.8mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ISO 4589-2 | 29 % | |
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| smoke density | NFF16-101 | I3 | |
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| density | ISO 1183/A | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | SOLVAY FRANCE/A 205F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 65.0 °C | |
| melting temperature | ISO 11357-3 | 263 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 205 °C |