PP Homopolymer RIALFILL H 15 S 40 T0 RIALTI ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
Impact strength of cantilever beam gap-20°CISO 180/1A2.1 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU18 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A2.5 kJ/m²
hardnessTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
Shore hardness邵氏D,15秒ISO 86878
Mechanical propertiesTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
Flexural modulus23°CISO 1784400 MPa
tensile strength 断裂,23°CISO 527-2/2028.0 MPa
Tensile strain断裂,23°CISO 527-2/205.0 %
tensile strength 屈服,23°CISO 527-2/2030.0 MPa
Tensile strain屈服,23°CISO 527-2/203.0 %
bending strength23°CISO 17848.0 MPa
flammabilityTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
UL flame retardant rating1.5mmUL 94HB
agingTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
Accelerated oven aging150°CISO 45776.3 day
physical property Test ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
Shrinkage rateTDISO 294-40.90 %
MDISO 294-40.90 %
ash contentISO 345140 %
Water absorption rate23°C,24hrISO 620.020 %
densityISO 11831.25 g/cm³
melt mass-flow rate230°C/2.16kgISO 113312 g/10min
Thermal performanceTest ConditionTest MethodRIALTI ITALY/RIALFILL H 15 S 40 T0
ball-indentation hardness125°CIEC 335通过
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B131 °C
vicat--ISO 306/A50154 °C
--ISO 306/B50100 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A80.0 °C
Linear coefficient of thermal expansionMDISO 11359-26E-05 cm/cm/°C