ABS POLYLAC® PA-716 CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
Charpy Notched Impact Strength23°CISO 17926 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTM D256240 J/m
23°C,6.40mmASTM D256210 J/m
Charpy Notched Impact Strength-30°CISO 17912 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A11 kJ/m²
23°CISO 180/1A25 kJ/m²
hardnessTest ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
Rockwell hardnessR级ASTM D785112
Mechanical propertiesTest ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
elongation断裂4ASTM D63825 %
tensile strength 屈服4ASTM D63843.6 MPa
bending strength--5ASTM D79068.4 MPa
Flexural modulus--6ISO 1781900 MPa
--5ASTM D7902340 MPa
elongation断裂ISO 527-2/5025 %
tensile strength 屈服ISO 527-2/5042.0 MPa
bending strength--6ISO 17865.0 MPa
tensile strength 断裂ISO 527-2/5031.0 MPa
flammabilityTest ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
Melt volume flow rate220°C/10.0kgISO 113333.0 cm³/10min
density23°CISO 11831.04 g/cm³
melt mass-flow rate200°C/5.0kgASTM D12383.5 g/10min
Shrinkage rateISO 294-40.40to0.70 %
density--3ASTM D7921.04 g/cm³
Thermal performanceTest ConditionTest MethodCHI MEI CORPORATION/POLYLAC® PA-716
Heat distortion temperature1.8MPa,未退火，HDTASTM D64885.0 °C
1.8MPa,退火，HDTASTM D64895.0 °C
vicat--ASTM D15257105 °C
--ISO 306/A50104 °C
Heat distortion temperature1.8MPa,退火，HDTISO 75-2/A97.0 °C
1.8MPa,未退火，HDTISO 75-2/A83.0 °C
vicat--ISO 306/B5096.0 °C
Linear coefficient of thermal expansionMDISO 11359-29.1E-05 cm/cm/°C