density

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

220°C/2.16kg

ISO1133

cm3/10min

7

Melt mass flow rate

220°C/2.16kg

ISO1133

g/10min

8

Shrinkage rate

TD

ISO294-4

%

1

Shrinkage rate

MD

ISO294-4

%

1

Water absorption rate

23°C,24hr

ISO62

%

0

Water absorption rate

饱和,23°C,2.00mm

ISO62

%

0

Water absorption rate

平衡,23°C,2.00mm,50%RH

ISO62

%

0

Nominal tensile fracture strain

ISO527-2

%

7

abrasion resistance

ISO4649

mm³

1

Tensile modulus

ISO527-2

Mpa

8

tensile strength

断裂

ISO527-2

Mpa

3

tensile strength

10%应变

ISO527-2

Mpa

5

tensile strength

50%应变

ISO527-2

Mpa

9

tensile strength

100%应变

ISO527-2

Mpa

1

tensile strength

300%应变

ISO527-2

Mpa

1

elongation

断裂

ISO527-2

%

>

Bending modulus

ISO178

Mpa

8

Glass transition temperature

ISO11357-2

°C

-

Brittle temperature

ISO974

°C

-

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

5

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

3

Melting temperature

ISO11357-3

°C

1

vicat softening point

--

ISO306/A50

°C

1

vicat softening point

--

ISO306/B50

°C

6

Linear coefficient of thermal expansion

MD：--

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

MD：-40to23°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：--

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40to23°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：EffectiveThermalDiffusivity

ISO11359-2

m²/s

5

Surface resistivity

IEC60093

ohms

4

Dielectric strength

IEC60243-1

KV/mm

1

Leakage Trace Index

IEC60112

V

6

Volume resistivity

IEC60093

ohms·cm

8

tear strength

横向流量

ISO34-1

kN/m

1

tear strength

流量

ISO34-1

kN/m

1

WaterVaporTransmission Rate

23°C,85%RH,25µm

DIS15106-1/-2

g/m²/24hr

6

Extreme Oxygen Index

ISO4589-2

%

2

Burning rate

1.00mm

ISO3795

mm/min

<