ABS ECO GP-22 MR70 INEOS STYRO KOREA
--
Electrical enclosure,Household appliances,electronic product
Impact resistance,Heat resistant deformatio
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Ball Pressure TestISO 2039-197.0 Mpa
Rockwell hardnessR-ScaleASTM D785103
thermal performanceTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Hot deformation temperature0.45MPa,AnnealedASTM D648104 °C
1.8MPa,UnannealedASTM D64877.8 °C
1.8MPa,AnnealedISO 75-2/A94.0 °C
0.45MPa,AnnealedISO 75-2/B99.0 °C
1.8MPa,AnnealedASTM D64898.9 °C
0.45MPa,UnannealedASTM D64890.6 °C
Linear coefficient of thermal expansionMDISO 11359-28.0E-5to1.1E-4 cm/cm/°C
thermal conductivityDIN 526120.17 W/m/K
Vicat softening temperature--ISO 306/B5096.0 °C
--ISO 306/A50105 °C
mechanical propertiesTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Bending modulusASTM D7902300 Mpa
bending strengthISO 17865.0 Mpa
ASTM D79065.0 Mpa
elongationBreakASTM D6382.6 %
Nominal tensile fracture strain23°CISO 527-210 %
Tensile modulusASTM D6382300 Mpa
ISO 527-22300 Mpa
Tensile strainYield,23°CISO 527-22.6 %
tensile strengthYield,23°CASTM D63845.0 Mpa
Yield,23°CISO 527-245.0 Mpa
Electrical performanceTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Dielectric constant1.00mm,1MHzASTM D1502.80
Dissipation factor1MHzIEC 602507.9E-03
100HzIEC 602504.8E-03
Relative permittivity100HzIEC 602502.90
1MHzIEC 602502.80
Surface resistivityIEC 600931E+13 ohms
Volume resistivityASTM D257>1.0E+15 ohms·cm
IEC 600931E+15 ohms·cm
Physical propertiesTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
densityISO 11831.04 g/cm³
ASTM D7921.04 g/cm³
melt mass-flow rate220°C/10.0kgASTM D123819 g/10min
200°C/5.0kgASTM D12381.5 g/10min
Melt Volume Flow Rate (MVR)220°C/10.0kgISO 113319.0 cm3/10min
230°C/3.8kgASTM D12384.80 cm3/10min
Shrinkage rateISO 294-40.40-0.70 %
MDASTM D9550.40-0.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.22 %
Saturation,23°CISO 621.0 %
Saturation,23°CASTM D5701.0 %
impact performanceTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Charpy Notched Impact Strength-30°CISO 1798.0 kJ/m²
23°CISO 17922 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/A8.0 kJ/m²
23°CISO 180/A26 kJ/m²
-18°CASTM D256100 J/m
23°CASTM D256300 J/m
-30°CASTM D25659 J/m
Impact strength of simply supported beam without notch-30°CISO 179100 kJ/m²
23°CISO 179180 kJ/m²
optical performanceTest ConditionTest MethodINEOS STYRO KOREA/ECO GP-22 MR70
Huangdu IndexDIN 616713 YI