PUR，Unspecified Ebalta MG 426 / Comp. A+B Ebalta Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 39to45 kJ/m² |
| hardness | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 7619 | 78to82 |
| Mechanical properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2090to2290 MPa | |
| bending strength | ISO 178 | 80.0to90.0 MPa |
| thermosetting | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Thermosetting components | 硬化法 | 按重量计算的混合比:100按容量计算的混合比:89 | |
| 树脂 | 按重量计算的混合比:100按容量计算的混合比:100 | ||
| 后固化时间(60°C) | 6.0to8.0 hr |
| Uncured Properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Viscosity | 25°C | 0.60to0.80 Pa·s | |
| STORAGE STABILITY | 20°C | 2.5to2.7 min | |
| density | 20°C | 1.15to1.19 g/cm³ | |
| Curing Time | 20°C | 1.5to2.0 hr |
| Thermal performance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta MG 426 / Comp. A+B |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 92.0to98.0 °C |