LLDPE LLDPE LF20185 JG Summit Petrochemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JG Summit Petrochemical Corporation/LLDPE LF20185 |
|---|---|---|---|
| Inflation ratio (BUR) | 2.00to4.00 |
| film | Test Condition | Test Method | JG Summit Petrochemical Corporation/LLDPE LF20185 |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 65 g |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 360 g |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 10.0 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 210 g |
| elongation | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 49 % |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 15.0 MPa |
| elongation | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 17 % |
| TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 520 % | |
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 185 MPa |
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 14.0 MPa |
| film thickness | 25 µm | ||
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 10.0 MPa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 500 % |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 202 MPa |
| optical performance | Test Condition | Test Method | JG Summit Petrochemical Corporation/LLDPE LF20185 |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 64 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTM D1003 | 19 % |
| physical property | Test Condition | Test Method | JG Summit Petrochemical Corporation/LLDPE LF20185 |
|---|---|---|---|
| density | ASTM D1505 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.0 g/10min |