Meltvolume-flowrate

220°C/10.0kg

ISO11332

cm3/10min

3

density

ASTMD792

g/cm³

1

density

ISO11832

kg/m3

1

Melt mass flow rate

200°C/5.0kg

ASTMD1238

g/10min

3

Melt mass flow rate

220°C/10.0kg

ASTMD1238

g/10min

2

Melt mass flow rate

230°C/3.8kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

ASTMD955

%

0

Water absorption rate

饱和

ISO622

%

0

Charpyimpactstrength

-30°C

ISO179/1eU2

kJ/m²

4

Charpynotchedimimpact string

23°C

ISO179/1eA2

kJ/m²

2

Charpy impact strength

23°C

ISO179/1eU2

kJ/m²

1

Charpy Notched Impact Strength

-30°C

ISO179/1eA2

kJ/m²

2

Tensile modulus

3.20mm

ASTMD638

Mpa

3

Tensile modulus

ISO527-22

Mpa

3

tensile strength

Yield,3.20mm

ASTMD638

Mpa

7

tensile strength

断裂

ISO527-22

Mpa

7

Tensile strain

Break,3.20mm

ASTMD638

%

6

elongation

断裂

ISO527-22

%

6

Bending modulus

3.20mm

ASTMD790

Mpa

3

bending strength

3.20mm

ASTMD790

Mpa

1

Impact strength of cantilever beam gap

-30°C,6.40mm

ASTMD256

J/m

9

Impact strength of cantilever beam gap

23°C,6.40mm

ASTMD256

J/m

9

RTI Imp

UL746

°C

5

RTIElec

UL746

°C

5

RTIStr

UL746

°C

5

Glass transition temperature

ISO11357-22

°C

1

Hot deformation temperature

1.8MPa,未退火,6.40mm

ASTMD648

°C

9

vicat softening point

ASTMD1525

°C

1

vicat softening point

50N

ISO3062

°C

1

Linear coefficient of thermal expansion

MD

ISO11359-22

cm/cm/°C

6

Linear coefficient of thermal expansion

TD

ISO11359-22

cm/cm/°C

6

Electrical strength

IEC60243-12

KV/mm

5

Surface resistivity

IEC600932

ohms

>

Volume resistivity

IEC600932

ohms·m

>