Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C7210A SABIC INNOVATIVE US
CYCOLAC™
Electronic field、Electrical field
High mobility、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A |
|---|---|---|---|
| Tensile strain | 5mm/min，屈服 | ASTM D638 | 3.6 % |
| Tensile modulus | 5mm/min | ASTM D638 | 35800 kgf/cm |
| bending strength | 1.3mm/min,50mm span | ASTM D790 | 1080 kgf/cm |
| Flexural modulus | 1.3mm/min,50mm span | ASTM D790 | 32000 kgf/cm |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D4812 | 190 cm-kgf/cm |
| tensile strength | 5mm/min，断裂 | ASTM D638 | 490 kgf/cm |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 17 cm-kgf/cm |
| tensile strength | 5mm/min，屈服 | ASTM D638 | 640 kgf/cm |
| Tensile strain | 5mm/min，断裂 | ASTM D638 | 80 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A |
|---|---|---|---|
| Shrinkage rate | flow, 3.2 mm | % | SABIC Method 0.3-0.5 |
| melt mass-flow rate | 260℃/2.16kgf | ASTM D1238 | 16.4 g/10min |
| density | ASTM D792 | 1.22 | |
| Shrinkage rate | xflow, 3.2 mm | % | SABIC Method 0.4－0.6 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A |
|---|---|---|---|
| Relative Heat Index (RTI) | UL 746B | 60 ℃ | |
| vicat | ASTM D1525 | 101 ℃ | |
| Linear coefficient of thermal expansion | xflow，-40℃to 40℃ | ASTM E 831 | 6.66E-05 1/℃ |
| UL flame retardant rating | 1.98mm | UL94 | 5VB |
| Heat distortion temperature | 1.82Mpa,未退火，HDT | ASTM D648 | 82 ℃ |
| Linear coefficient of thermal expansion | flow，-40℃to 40℃ | ASTM E 831 | 5.94E-05 1/℃ |
| Heat distortion temperature | 0.45Mpa,未退火，HDT | ASTM D648 | 92 ℃ |
| UL flame retardant rating | 1.19mm | UL94 | V-0 |