Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PES JFL-4036 SABIC INNOVATIVE US
LNP™ THERMOCOMP™ 
Electronic field、mechanical、Bearing retainer
High temperature creep re、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/JFL-4036
Suspended wall beam without notch impact strength23°CASTM D4812360 J/m
23°C3ISO 180/1U24 kJ/m²
Dart impact--ISO 6603-22.47 J
23°C,EnergyatPeakLoadASTM D37639.40 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/JFL-4036
Tensile modulus--2ASTM D63810200 Mpa
tensile strength 断裂ASTM D638129 Mpa
断裂ISO 527-289.0 Mpa
Flexural modulus--ISO 17810800 Mpa
Wear factorWasherASTM D3702Modified60.0 10^-10in^5-min/ft-lb-hr
bending strength--ISO 178138 Mpa
elongation断裂ASTM D6381.9 %
bending strength--ASTM D790179 Mpa
coefficient of frictionStaticASTM D3702Modified0.36
Tensile modulus--ISO 527-2/19540 Mpa
coefficient of frictionDynamicASTM D3702Modified0.46
Flexural modulus--ASTM D7909930 Mpa
elongation断裂ISO 527-21.5 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/JFL-4036
Shrinkage rateMD:24小时ISO 294-40.10-0.30 %
Water absorption rate24hr,50%RHASTM D5700.29 %
Shrinkage rateTD:24小时ASTM D9550.30-0.60 %
Water absorption rate平衡,23°C,50%RHISO 620.50 %
Shrinkage rateMD:24小时ASTM D9550.10-0.40 %
TD:24小时ISO 294-40.30-0.60 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/JFL-4036
Heat distortion temperature1.8MPa,未退火,64.0mm跨距4，HDTISO 75-2/Af210 °C
Linear coefficient of thermal expansionTD:-40到40°CASTME8313.5E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648208 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8312.3E-05 cm/cm/°C