Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 6030G HS BK BASF GERMANY
Ultramid®
Electrical enclosure、film
Oil resistant、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 54 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| tensile strength | 断裂,-40°C | ISO 527-2 | 220 Mpa |
| 断裂,80°C | ISO 527-2 | 80.0 Mpa | |
| Tensile modulus | 80°C | ISO 527-2 | 3820 Mpa |
| 23°C | ISO 527-2 | 9580 Mpa | |
| tensile strength | 断裂,23°C | ISO 527-2 | 155 Mpa |
| Rockwell hardness | ASTM D785 | 121 | |
| Tensile modulus | -40°C | ISO 527-2 | 8740 Mpa |
| 150°C | ISO 527-2 | 2890 Mpa | |
| 120°C | ISO 527-2 | 2730 Mpa | |
| tensile strength | 断裂,120°C | ISO 527-2 | 65.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 230 Mpa |
| tensile strength | 断裂,150°C | ISO 527-2 | 60.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 8070 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm |
| other | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| characteristic | 可加工性良好 热稳定 良好的流动性 | ||
| purpose | 护罩 支架 家具 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 |
| flammability | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 1.1 % |
| 平衡,23°C,50%RH | ISO 62 | 1.9 % | |
| 饱和,23°C | ISO 62 | 6.7 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/6030G HS BK |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Str | 0.8mm | UL 746 | 130 °C |
| RTI Elec | 3.0mm | UL 746 | 140 °C |
| RTI Imp | 3.0mm | UL 746 | 120 °C |
| melting temperature | ISO 3146 | 220 °C | |
| RTI Elec | 0.8mm | UL 746 | 130 °C |
| RTI Imp | 0.8mm | UL 746 | 115 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 219 °C |
| Linear coefficient of thermal expansion | MD | 2.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| RTI Str | 1.5mm | UL 746 | 140 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | TD | 6.7E-05 cm/cm/°C |