PA6 FRIANYL® B3 VNGF25 V0 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
Charpy Notched Impact Strength23°CISO 179/1eA8.0 kJ/m²
-30°CISO 179/1eA6.5 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
-30°CISO 179/1eU45 kJ/m²
Electrical performanceTest ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
needle flame test1.00mmIEC 60695-11-5通过
Compared to the Leakage Tracking Index (CTI)3.20mm,解决方案AIEC 60112PLC 0
needle flame test2.00mmIEC 60695-11-5通过
Volume resistivity23°CIEC 600931E+15 ohms·cm
dielectric strength2.00mmIEC 60243-118 kV/mm
Surface ResistivityIEC 600931E+13 ohms
Mechanical propertiesTest ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
Tensile strain断裂,23°CISO 527-23.0 %
Tensile modulus23°CISO 527-29000 MPa
tensile strength 屈服,23°CISO 527-2135 MPa
flammabilityTest ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
Burning wire flammability index0.8mmIEC 60695-2-12960 °C
3.2mmIEC 60695-2-12960 °C
UL flame retardant rating3.2mmUL 94V-0
0.8mmUL 94V-0
Limiting Oxygen IndexISO 4589-232 %
UL flame retardant rating1.6mmUL 94V-0
0.40mmUL 94V-0
physical property Test ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
Shrinkage rateTD:23°CISO 294-40.80 %
density23°CISO 11831.38 g/cm³
Water absorption rate23°C,24hrISO 621.9 %
Shrinkage rateMD:23°CISO 294-40.30 %
Water absorption rate饱和,23°CISO 625.0 %
Thermal performanceTest ConditionTest MethodCelanese Corporation/FRIANYL® B3 VNGF25 V0
Continuous use temperatureIEC 60216125 °C
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B>250 °C
1.8MPa,未退火,HDTISO 75-2/A>250 °C
ball-indentation hardness165°CIEC 60695-10-2通过
125°CIEC 60695-10-2通过