Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC S-3000VR MITSUBISHI THAILAND
IUPILON™ 
Automotive sector、Electrical appliances、Electronic field、Electrical field
Weather resistance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/S-3000VR
Charpy Notched Impact Strength23°CISO 17967 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/S-3000VR
Tensile modulusISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-2120 %
bending strengthISO 17893.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-26.7 %
tensile strength 屈服ISO 527-262.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/S-3000VR
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor1MHzIEC 602509E-03
physical property Test ConditionTest MethodMITSUBISHI THAILAND/S-3000VR
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 113314.0 cm3/10min
Shrinkage rateMD:3.20mm0.50-0.70 %
Water absorption rate饱和,23°CISO 620.24 %
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 113315 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/S-3000VR
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B139 °C
1.8MPa,未退火，HDTISO 75-2/A124 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C