Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 357X-7001 SABIC INNOVATIVE US
VALOX™ 
Electrical appliances,Plastic bag,Casters,Household goods
Flame retardant,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
Ball Pressure TestH358/30ISO 2039-1115 Mpa
Rockwell hardnessR-SaleISO 2039-2115
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
0.45MPa, unannealed, 100mm spanISO 75-2/Be135 °C
0.45MPa, unannealed, 3.20mmASTM D648130 °C
0.45MPa, unannealed, 64.0mm spanISO 75-2/Bf130 °C
1.8MPa, unannealed, 100mm spanISO 75-2/Ae85.0 °C
1.8MPa, unannealed, 3.20mmASTM D64885.0 °C
1.8MPa, unannealed, 64.0mm span ofISO 75-2/Af85.0 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Flow: 23 to 80 ° C23to80℃ISO 11359-21E-04 cm/cm/°C
Flow: -40 to 40 ° CASTME8319.2E-05 cm/cm/°C
Horizontal: 23 to 80 ° CAcross Flow, 23to80℃ISO 11359-21E-04 cm/cm/°C
Horizontal: -40 to 40 ° CAcross Flow, -40to40℃ASTME8318.4E-05 cm/cm/°C
RTIUL 746140 °C
RTI ElecUL 746120 °C
RTI ImpUL 746120 °C
thermal conductivityISO 83020.17 W/m/K
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
--10ISO 17880.0 Mpa
--3ASTM D6382000 Mpa
50.0mm spanASTM D7902100 Mpa
--9ISO 1782000 Mpa
crackISO 527-2/5030 %
ASTM D63840.0 Mpa
ASTM D63830 %
ISO 527-2/5040.0 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method33.0 mg
yieldASTM D6385.0 %
ASTM D63850.0 Mpa
ISO 527-2/505.0 %
ISO 527-2/5050.0 Mpa
Yield, 50.0mm spanASTM D79078.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
0.800mm, in oilIEC 60243-134 KV/mm
1.60mm,inOilASTM D14925 KV/mm
1.60mm, in oilIEC 60243-125 KV/mm
1MHz1MHzASTM D1500.013
1MHzIEC 602501.3E-03
1MHzASTMD1503.00
3.20mm, inoilASTM D14917 KV/mm
3.20mm, in oilIEC 60243-117 KV/mm
50Hz50HzIEC 602502E-03
60Hz60HzIEC 602502E-03
Arc resistanceASTM D495PLC6
Compared to the anti leakage trace index--IEC 60112PLC 3
SolutionBIEC 60112PLC 4
CTIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 3
Hot wire ignitionHWIUL 746PLC 3
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTMD257>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
melt mass-flow rate265°C/5.0kgASTM D123813 g/10min
266°C/5.0kgASTM D123813 g/10min
250°C/5.0kgASTM D12389.6 g/10min
Melt Volume Flow Rate (MVR)265°C/5.0kgISO 113310.0 cm3/10min
250°C/5.0kgISO 11338.00 cm3/10min
Shrinkage rateTD2Internal Method0.90-1.8 %
MD:3.20mmInternal Method1.0-1.4 %
MD1Internal Method1.1-1.8 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Saturation,23°CISO 620.50 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
0°CASTM D256190 J/m
ISO 180/1A20 kJ/m²
23°CISO 179/2C40 kJ/m²
ASTM D256500 J/m
ISO 179/1eA45 kJ/m²
ISO 180/1A40 kJ/m²
-30°CASTM D256150 J/m
ISO 180/1A10 kJ/m²
ISO 179/1eA20 kJ/m²
Dart impact23°C,TotalEnergyASTM D376335.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CASTMD4812无断裂
-30°CASTMD4812无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
Burning wire flammability index1.00mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-230 %
UL flame retardant rating0.750mmUL 94V-0
2.50mmUL 945VA
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE US/357X-7001
Melt viscosity260°C,1500sec^-1ISO 11443310 Pa·s