Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 5000S TAIDA TAIWAN
TAITALAC®
Charger casing、Industrial applications、rope、Bag、Monofilament、For audio tapes、clock、Household products、Recording tape case, etc、Electrical appliances、Household goods、Audiotape
High rigidity、antioxidant、Good tensile strength、High steel type、Injection molding、High rigidity and impact
UL
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 150 J/m |
| 23°C,3.18mm | ASTMD256 | 160 J/m |
| hardness | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 119 |
| Basic performance | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.3 wt% | |
| density | ASTM D-792 | 1.04 |
| Mechanical properties | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| IZOD notch impact strength | 23℃1/2" | ASTM D-256 | 13 (2.4) kg.cm/cm(ft.1b/in) |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 380 kg/cm |
| tensile strength | 屈服,23°C,3.18mm | ASTMD638 | 46.9 Mpa |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 6800 psi |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 37.2 Mpa |
| elongation | 断裂,23°C,3.18mm | ASTMD638 | 20 % |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 420000 psi |
| Flexural modulus | 23°C | ASTMD790 | 2900 Mpa |
| Flexural Strength | 23℃ 2.8mm/min | ASTM D-790 | 800 kg/cm |
| bending strength | 屈服,23°C | ASTMD790 | 78.6 Mpa |
| Flexural Strength | 23℃ 2.8mm/min | ASTM D-790 | 11400 psi |
| Rockwell hardness | 119 | ||
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 30000 kg/cm |
| elongation at break | 1/8" | ASTM D-638 | 20 % |
| IZOD notch impact strength | 23℃1/8" | ASTM D-256 | 16 (2.9) kg.cm/cm(ft.1b/in) |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 5400 psi |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 480 kg/cm |
| Electrical performance | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| High arc combustion index (HAI) | 1.57mm | UL746 | 15.0 |
| High voltage arc ignition resistance index | 1.57mm | UL746 | 0.00 mm/min |
| Arc generation rate | UL-746A | 0 in/min | |
| Hot-wireIgnition | 1.57mm | UL746 | 15 sec |
| arc resistance | UL-746A | 15 Arcs |
| processability | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| rti | UL-746B | 60 °C |
| flammability | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 2.3 g/10min |
| density | ASTMD792 | 1.04 g/cm³ | |
| Shrinkage rate | ASTM D-955 | 0.4 % | |
| MD | ASTMD955 | <0.40 % | |
| Water absorption rate | 24hr | ASTMD570 | <0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | TAIDA TAIWAN/5000S |
|---|---|---|---|
| Resistance to hot wire combustion | UL-746A | 15 Sece | |
| RTI Elec | 1.6mm | UL746 | 60.0 °C |
| 未退火 | ASTM D-648 | 89 (192) ℃(F) | |
| 1.8MPa,未退火,12.7mm | ASTMD648 | 83.0 °C | |
| RTI Str | 1.6mm | UL746 | 60.0 °C |
| vicat | ASTM D-1525 | 104 °C | |
| RTI Imp | 1.6mm | UL746 | 60.0 °C |
| vicat | ASTMD15254 | 104 °C | |
| UL flame retardant rating | UL94 | HB |