Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE 2049G DOW THAILAND
ELITE™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| Film Resilience (MD) | 38.1um | ASTM D-882 | 128 J/cm4 |
| Film Resilience (TD) | 38.1um | ASTM D-882 | 140 J/cm³ |
| Film Piercing Resistance Movement | 38.1um | Internal Method | 3.06 J/cm³ |
| film | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| tensile strength | TD:断裂,38µm | ASTMD882 | 42.3 Mpa |
| Secant modulus | 2%正割,MD:38µm | ASTMD882 | 235 Mpa |
| tensile strength | TD:屈服,38µm | ASTMD882 | 14.7 Mpa |
| Elmondov tear strength | MD:38µm | ASTMD1922 | 250 g |
| Secant modulus | 2%正割,TD:38µm | ASTMD882 | 281 Mpa |
| Elmondov tear strength | TD:38µm | ASTMD1922 | 590 g |
| tensile strength | MD:断裂,38µm | ASTMD882 | 47.8 Mpa |
| Film thickness - tested | 38 µm | ||
| Membrane puncture resistance | 38µm | 内部方法 | 3.06 J/cm³ |
| elongation | TD:断裂,38µm | ASTMD882 | 740 % |
| tensile strength | MD:屈服,38µm | ASTMD882 | 13.2 Mpa |
| elongation | MD:断裂,38µm | ASTMD882 | 630 % |
| film strength | TD:38µm | ASTMD882 | 140 J/cm³ |
| MD:38µm | ASTMD882 | 128 J/cm³ | |
| Falling hammer impact | 25µm | ASTMD1709A | 220 g |
| Basic performance | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| film thickness | 38.1 um | ||
| density | ASTM D-792 | 0.926 g/m3 | |
| melt mass-flow rate | ASTM D-1238 | 1 g/10min |
| Mechanical properties | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| Tangent modulus (TD) | 2% Secant，38.1um | ASTM D-882 | 281 Mpa |
| Tensile elongation at break (MD) | 38.1um | ASTM D-882 | 630 % |
| Elmendorf Tear Strength (TD) | 38.1um | ASTM D-1922 | 590 g |
| Tensile yield strength (MD) | 38.1um | ASTM D-882 | 13.2 Mpa |
| Elmendorf Tear Strength (MD) | 38.1um | ASTM D-1922 | 250 |
| Tensile yield strength (TD) | 38.1um | ASTM D-882 | 14.7 Mpa |
| Tangent modulus (MD) | 2% Secant，38.1um | ASTM D-882 | 235 Mpa |
| Tensile elongation at break (TD) | 38.1um | ASTM D-882 | 740 % |
| Falling hammer impact | 25.4um | ASTM D-1709A | 220 g |
| Tensile strength at break (MD) | 38.1um | ASTM D-882 | 47.8 Mpa |
| Tensile fracture strength (TD) | 38.1um | ASTM D-882 | 42.3 Mpa |
| optical performance | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| Haze ratio | 38.1µm | ASTMD1003 | 9.0 % |
| gloss | 45°，38.1um | ASTM D-2457 | 80 |
| Haze ratio | 38.1um | ASTM D-1003 | 9 % |
| gloss | 45°,38.1µm | ASTMD2457 | 80 |
| processability | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| Melt Temperature | 207-216 °C |
| physical property | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 1.0 g/10min |
| density | ASTMD792 | 0.926 g/cm³ |
| Thermal performance | Test Condition | Test Method | DOW THAILAND/2049G |
|---|---|---|---|
| vicat | ASTM D-1525 | 112 °C | |
| ASTMD1525 | 112 °C | ||
| 内部方法 | 121 °C | ||
| Melting temperature | Internal Method | 121 °C |