POM C9021TF5 CELANESE USA
HOSTAFORM®
Household appliances,Household appliances,Automotive sector,Fitness equipment,Thin walled products
wear resistant,currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| melting temperature | DSC,10 K/min | ISO 3146 method C1b | 166 °C |
| vicat | VST/B/50 | ISO 306 | 150 °C |
| Linear coefficient of thermal expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 µm/m-℃ |
| Heat Deflection Temperature | 1.8MPa，HDT | ISO 75 part 1/2 | 100 °C |
| Basic performance | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| Water absorption rate | 23℃and50%RH | ISO 62 | 0.2 % |
| melt mass-flow rate | 8.5cm | ISO 1133 | 12.07 g/10min |
| Water absorption rate | 饱和23℃ | ISO 62 | 0.75 % |
| density | ISO 1183 | 1.42 g/cm |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| Tensile creep modulus | 1000 hours | ISO 899 part 1 | 1200 Mpa |
| Impact strength of simply supported beam without notch | 低温-30℃ | ISO 179 1eU | 12 J/cm |
| Elongation at break | 50mm/min | ISO 527 part 1/2 | 20 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179 1eA | 0.6 J/cm |
| Tensile modulus | 1mm/min | ISO 527 part 1/2 | 2800 Mpa |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179 1eU | 12.0 J/cm |
| flexural modulus | ISO 178 | 2700 Mpa | |
| ball-indentation hardness | 30秒数值 | ISO 2039 part 1 | 140 Mpa |
| elongation | 伸长率 | ISO 527 part 1/2 | 9.0 % |
| Charpy Notched Impact Strength | 低温-30℃ | ISO 179 1eA | 0.6 J/cm |
| Tensile creep modulus | 1 hour | ISO 899 part 1 | 2400 Mpa |
| tensile strength | 50mm/min，屈服 | ISO 527 part 1/2 | 65 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| Dissipation Factor | 低频100 Hz | IEC 60250 | 0.0025 |
| dielectric strength | IEC 60243 part 1 | 35 KV/mm | |
| dielectric constant | 低频100 Hz | IEC 60250 | 4.20 |
| Dissipation Factor | IEC 60250 | 0.008 1 MHz | |
| dielectric constant | 1 MHz | IEC 60250 | 4.20 |
| other | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| characteristic | 注塑成型 |
| Physical properties | Test Condition | Test Method | CELANESE USA/C9021TF5 |
|---|---|---|---|
| shrinkage rate | ASTM D955 | - % | |
| density | ASTM D792/ISO 1183 | 1440 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 8.5 g/10min |