Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE DFL-4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Lighting applications
Easy to form、Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 |
|---|---|---|---|
| 23°C | ASTMD256 | 150 J/m | |
| ASTMD4812 | 740 J/m | ||
| 23°C8 | ISO180/1U | 49 kJ/m² | |
| 23°C7 | ISO180/1A | 14 kJ/m² | |
| 23°C,TotalEnergy | ASTMD3763 | 19.6 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 |
|---|---|---|---|
| Fracture 2 | ASTMD638 | 95.0 Mpa | |
| fracture | ISO527-2/5 | 3.1 % | |
| Fracture, 50.0mm span 6 | ASTMD790 | 145 Mpa | |
| 50.0mm span 4 | ASTMD790 | 6320 Mpa | |
| --1 | ASTMD638 | 7190 Mpa | |
| 与自身-静态 | ASTMD3702Modified | 0.50 | |
| yield | ISO527-2/5 | 2.8 % | |
| fracture | ISO527-2/5 | 93.0 Mpa | |
| Fracture 3 | ASTMD638 | 2.7 % | |
| 与自身-动态 | ASTMD3702Modified | 0.46 | |
| Wear factor | Ring | ASTMD3702Modified | 13.0 10^-10in^5-min/ft-lb-hr |
| Washer | ASTMD3702Modified | 89.0 10^-10in^5-min/ft-lb-hr | |
| --5 | ISO178 | 6200 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ASTMD955 | 0.020到0.040 % |
| Balance, 23 ° C, 50% RH | ISO62 | 0.13 % | |
| Shrinkage rate | TD:24小时 | ASTMD955 | 0.20到0.40 % |
| 24hr,50%RH | ASTMD570 | 0.090 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 |
|---|---|---|---|
| TD:-30到30°C | ASTMD696 | 6.3E-05 cm/cm/°C | |
| 1.8MPa, Unanealed, 64.0mm span 10 | ISO75-2/Af | 141 °C | |
| MD:-30到30°C | ASTMD696 | 3.7E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 64.0mm span 9 | ISO75-2/Bf | 146 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTMD648 | 146 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTMD648 | 142 °C |