Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 E-RUNG60 UNITIKA JAPAN
UNITIKA
Electrical components、Vehicle electronics、Electronic field、Electrical field
Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/E-RUNG60 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 19000 Mpa | |
| Rockwell hardness | R | ISO 2039-2 | 120 |
| Tensile stress | 断裂 | ISO 527-2 | 240 Mpa |
| bending strength | ISO 178 | 370 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 80 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| Flexural modulus | ISO 178 | 18600 Mpa |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/E-RUNG60 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 | |
| dielectric strength | 1.0mm | IEC 60243-1 | 35 |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/E-RUNG60 |
|---|---|---|---|
| Shrinkage rate | MD，3.2mm | ISO 294-4 | 0.1 % |
| 横向，3.2mm | ISO 294-4 | 0.3 % | |
| Water absorption rate | 23℃，50%RH | ISO 62 | 0.7 % |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/E-RUNG60 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 175-2/A | 225 °C |
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000025 cm/cm/℃ | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 175-2/B | 250 °C |
Contact Us
Get App