Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA/PC TA-35 KMJ1004A UMG JAPAN
UMG ALLOY®
--
High impact resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/TA-35 KMJ1004A |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 105 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/TA-35 KMJ1004A |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 73.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 1900 Mpa |
| tensile strength | 23°C | ISO 527-2 | 49.0 Mpa |
| physical property | Test Condition | Test Method | UMG JAPAN/TA-35 KMJ1004A |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.50-0.70 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 7.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/TA-35 KMJ1004A |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 106 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |