PA6 NILAMID® B3 H CF30 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
-30°CISO 179/1eA8.5 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU80 kJ/m²
-30°CISO 179/1eU68 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/A11 kJ/m²
-30°CISO 180/A9.0 kJ/m²
Mechanical propertiesTest ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
Tensile strain断裂,23°CISO 527-22.0 %
tensile strength 屈服,23°CISO 527-2220 MPa
Tensile modulus23°CISO 527-222000 MPa
Electrical performanceTest ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
Compared to the Leakage Tracking Index (CTI)3.20mm,解决方案AIEC 60112PLC 4
Volume resistivity23°CIEC 600931E+03 ohms·cm
dielectric strength2.00mmIEC 60243-12.0 kV/mm
Surface ResistivityIEC 600931E+02 ohms
flammabilityTest ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
UL flame retardant rating3.2mmUL 94HB
0.8mmUL 94HB
Limiting Oxygen IndexISO 4589-225 %
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
density23°CISO 11831.27 g/cm³
Shrinkage rateTD:23°CISO 294-40.30 %
Water absorption rate23°C,24hrISO 620.80 %
Shrinkage rateMD:23°CISO 294-40.15 %
Water absorption rate饱和,23°CISO 625.0 %
Thermal performanceTest ConditionTest MethodCelanese Corporation/NILAMID® B3 H CF30
Continuous use temperatureIEC 60216130 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B221 °C
1.8MPa,未退火，HDTISO 75-2/A210 °C
ball-indentation hardness165°CIEC 60695-10-2通过
125°CIEC 60695-10-2通过