PC GPN2040DF BK9001 MITSUBISHI ENGINEERING JAPAN
IUPILON™
fibre,Fiber grade
High mobility,enhance,Flame retardant,Filler: Glass fiber reinf,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GPN2040DF BK9001 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 150 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 10200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9900 Mpa |
| elongation at break | 23°C | ISO 527-2 | 1.5 % |
| tensile strength | 23°C | ISO 527-2 | 82.0 Mpa |
| Flame retardant performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GPN2040DF BK9001 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.60mm | |
| UL -94 | V-0.5VA 3.00mm |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GPN2040DF BK9001 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.08 % |
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 9.6 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GPN2040DF BK9001 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 117 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 123 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2.9E-05 cm/cm/°C |