Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA6 8233GHS-BK-102 BASF GERMANY
Ultramid®
Helmet、Automotive Applications、Engine parts
Thermal stability、high strength、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
Dart impact | 23°C | 内部方法 | 4.07 J |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 65 kJ/m² |
hardness | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 121 |
Mechanical properties | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
tensile strength | 断裂,-40°C | ISO 527-2 | 230 Mpa |
elongation | Break,121°C | ASTM D638 | 7.0 % |
bending strength | ASTM D790/ISO 178 | 179/26000 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 断裂,80°C | ISO 527-2 | 90.0 Mpa |
Tensile modulus | 80°C | ISO 527-2 | 4820 Mpa |
bending strength | 23°C | ASTM D790 | 280 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 10200 Mpa |
tensile strength | 断裂,80°C | ASTM D638 | 90.0 Mpa |
断裂,23°C | ISO 527-2 | 170 Mpa | |
Tensile modulus | 150°C | ISO 527-2 | 3560 Mpa |
tensile strength | 断裂,150°C | ISO 527-2 | 60.0 Mpa |
Flexural modulus | 23°C | ISO 178 | 8500 Mpa |
tensile strength | Break,121°C | ASTM D638 | 70.0 Mpa |
Flexural modulus | ASTM D790/ISO 178 | 5130/744000 kg/cm²(MPa)[Lb/in²] | |
Tensile modulus | -40°C | ISO 527-2 | 10300 Mpa |
tensile strength | 断裂,23°C | ASTM D638 | 180 Mpa |
ASTM D638/ISO 527 | 125/18100 kg/cm²(MPa)[Lb/in²] | ||
Tensile modulus | 120°C | ISO 527-2 | 4010 Mpa |
tensile strength | 断裂,120°C | ISO 527-2 | 70.0 Mpa |
Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
bending strength | 23°C | ISO 178 | 245 Mpa |
elongation | 断裂,-40°C | ASTM D638 | 3.0 % |
断裂,80°C | ASTM D638 | 7.0 % | |
Flexural modulus | 23°C | ASTM D790 | 8990 Mpa |
tensile strength | 断裂,-40°C | ASTM D638 | 230 Mpa |
elongation | 断裂,23°C | ASTM D638 | 3.5 % |
Physical properties | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.39 |
flammability | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
UL flame retardant rating | 3.0mm | UL 94 | HB |
1.5mm | UL 94 | HB | |
0.60mm | UL 94 | HB |
physical property | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
Shrinkage rate | MD:3.18mm | 0.30 % | |
Water absorption rate | 饱和 | ASTM D570 | 6.4 % |
24hr | ASTM D570 | 1.1 % | |
23°C,24hr | ISO 62 | 1.1 % | |
平衡,50%RH | ASTM D570 | 1.8 % | |
平衡,23°C,50%RH | ISO 62 | 1.8 % | |
饱和,23°C | ISO 62 | 6.4 % |
Thermal performance | Test Condition | Test Method | BASF GERMANY/8233GHS-BK-102 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 208 °C |
RTI Imp | 1.5mm | UL 746 | 115 °C |
melting temperature | ASTM D3418 | 220 °C | |
RTI Elec | 0.71mm | UL 746 | 130 °C |
3.0mm | UL 746 | 140 °C | |
RTI Imp | 3.0mm | UL 746 | 120 °C |
melting temperature | ISO 3146 | 220 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648 | 218 °C |
0.45MPa,未退火,HDT | ISO 75-2/B | 215 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 205 °C | |
RTI Str | 1.5mm | UL 746 | 140 °C |
3.0mm | UL 746 | 140 °C | |
RTI Elec | 1.5mm | UL 746 | 140 °C |
Linear coefficient of thermal expansion | MD | ASTME831 | 3.8E-05 cm/cm/°C |
RTI Imp | 0.71mm | UL 746 | 115 °C |
RTI Str | 0.71mm | UL 746 | 130 °C |