PA66 9A20000 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 4.0 kJ/m² |
| 23°C | ISO 179/B | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| 23°C | ISO 180/1A | 5.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 5.0 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 85.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/5 | 3200 MPa |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| flammability | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| Shrinkage rate | MD | 1.4 % | |
| water content | ISO 960 | <2000 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.7 % |
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | TD | 1.4 % |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9A20000 |
|---|---|---|---|
| melting temperature | ISO 11357 | 262 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |