PP X M2 V05 LYONDELLBASELL HOLAND
Moplen
Automotive interior equip、Automotive interior parts、Automotive sector
High rigidity、Mineral reinforcement、Mineral filler、20% filler by weight、High rigidity、copolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| melt flow rate | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M2 V05 |
|---|---|---|---|
| Tensile strain | 断裂 | 30 |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M2 V05 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 22.0 Mpa |
| Tensile modulus | 正割 | ISO 527-2 | 2000 Mpa |
| Impact strength of simply supported beam without notch | 0℃ | ISO 179/1eU | 39 kJ/m² |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.0 % |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M2 V05 |
|---|---|---|---|
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 20 g/10 min |
| 球压硬度，H 358/30 | ISO 2039-1 | 60.0 Mpa | |
| 溶化体积流率，230℃/2.16 kg | ISO 1133 | 23.5 cm3/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M2 V05 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 110 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 60.0 °C |