Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2200R SABIC INNOVATIVE SAUDI
SABIC®
--
High impact resistance、High temperature resistan、transparent、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 55.0 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| -30°C8 | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 63.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| elongation | 断裂4 | ASTM D638 | > 70 % |
| Tensile modulus | --3 | ASTM D638 | 2350 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 2300 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| 断裂 | ISO 527-2/50 | > 70 % | |
| 屈服4 | ASTM D638 | 6.0 % | |
| bending strength | --6,7 | ISO 178 | 90.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 2300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 90.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| dielectric strength | 1.60 mm | ASTM D149 | 27 KV/mm |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.0E-3 |
| dielectric constant | 1 MHz | ASTM D150 | 3.00 |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.010 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| refractive index | ISO 179/leA | 1.586 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 to 90.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.35 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 21.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 22 g/10 min |
| Shrinkage rate | --2，Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| thermal conductivity | ASTM C177 | 0.20 W/m/K | |
| vicat | ISO 306/B50 | 140 °C | |
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 7.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 133 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDT | ISO 75-2/Af | 122 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 23 到 80°C，流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDT | ISO 75-2/Bf | 133 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 122 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/2200R |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the rear of the barrel | 260 to 280 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 280 to 300 °C | ||
| Temperature | 80 to 100 °C | ||
| Spray nozzle temperature | 270 to 290 °C |