PC HPX4EU SABIC INNOVATIVE US
LEXAN™
Drug application,Medical devices,Medical and nursing supplies,medicine,Medical/nursing supplies
Middle flow,Biocompatibility,Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 82.4 J |
| -30°C,TotalEnergy | ASTM D3763 | 85.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 90 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| yield | ASTM D638 | 58.0 Mpa | |
| ASTM D638 | 5.8 % | ||
| ISO 527-2/50 | 57.9 Mpa | ||
| Yield, 50.0mm span | ASTM D790 | 94.3 Mpa | |
| fracture | ISO 527-2/50 | 61.5 Mpa | |
| ASTM D638 | 64.1 Mpa | ||
| ISO 527-2/50 | 120 % | ||
| ASTM D638 | 130 % | ||
| yield | ISO 527-2/50 | 5.5 % | |
| --8 | ISO 178 | 90.2 Mpa | |
| 50.0mm span | ASTM D790 | 2220 Mpa | |
| --1 | ASTM D638 | 2220 Mpa | |
| --7 | ISO 178 | 2150 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 3.0 % |
| transmissivity | 2540µm | ASTM D1003 | 82.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Hot filament ignition temperature | 0.800mm | IEC 60695-2-13 | 825 °C |
| 3.00mm | IEC 60695-2-13 | 825 °C | |
| UL flame retardant rating | 2.50mm | UL 94 | V-2 |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.50mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40-0.80 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.50 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.093 % |
| 饱和,23°C | ISO 62 | 0.24 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.40-0.80 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| Horizontal: -40 to 95 ° C | 横向, -40到95℃ | ASTME831 | 7.9E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 7.9E-05 cm/cm/°C |
| Flow: -40 to 95 ° C | -40到95℃ | ASTME831 | 7.2E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 119 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 124 °C | |
| RTI | UL 746 | 130 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 130 °C |