Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC KG-10MRA KOTEC JAPAN
CARBO TEX
Fiber grade
Flame retardant,high viscosity,Filler: Glass fiber reinf,10% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| bending strength | - | ASTM D790 | 17100 Ibf/in2 |
| ASTM D790/ISO 178 | 120 kg/cm²(MPa)[Lb/in²] | ||
| tensile strength | - | ASTM D638 | 74 Mpa |
| Flexural modulus | - | ASTM D790 | 3530 Mpa |
| - | ASTM D790 | 512000 Ibf/in2 | |
| ASTM D790/ISO 178 | 36000 kg/cm²(MPa)[Lb/in²] | ||
| bending strength | - | ASTM D790 | 118 Mpa |
| ASTM D790 | 118 Mpa | ||
| Flexural modulus | - | ASTM D790 | 36000 Kgf/cm2 |
| tensile strength | 断裂 | ASTM D638 | 74.0 Mpa |
| elongation at break | ASTM D638/ISO 527 | 5.0 % | |
| tensile strength | ASTM D638/ISO 527 | 750 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790 | 3530 Mpa | |
| Impact strength of cantilever beam gap | - | ASTM D256 | 1.8 ft.ibf/in |
| bending strength | - | ASTM D790 | 1200 Kgf/cm2 |
| elongation | 断裂 | ASTM D638 | 5.0 % |
| Impact strength of cantilever beam gap | - | ASTM D256 | 10 Kgf.cm/cm |
| - | ASTM D256 | 100 J/m | |
| tensile strength | - | ASTM D638 | 1100 Ibf/in2 |
| - | ASTM D638 | 750 Kgf/cm2 |
| Electrical performance | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 8E-03 |
| Volume resistivity | ASTM D257 | 1016 Ω.cm | |
| dielectric constant | 1MHz | ASTM D150 | 3.20 |
| dielectric strength | 1.60mm | ASTM D149 | 20 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 10^16 Ω.cm | |
| arc resistance | ASTM D495 | 110 sec |
| other | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| characteristic | 增强玻璃纤维 |
| optical performance | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| Haze ratio | 3.00mm | ASTM D1003 | Translucent |
| Physical properties | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.27 |
| flammability | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30-0.50 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | <0.20 % |
| Thermal performance | Test Condition | Test Method | KOTEC JAPAN/KG-10MRA |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 140 °C |
| HDT | ASTM D648/ISO 75 | 140 ℃（℉） | |
| 18.6kg/cm2，HDT | ASTM D648 | 140 °C | |
| 18.6kg/cm2，HDT | ASTM D648 | 284 ℉ | |
| heat resistance | ASTM D257 | V-0 |