Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G35HSL BK262 DUPONT SHENZHEN
Zytel®
Automotive components、Electronic and Electrical
lubrication、High temperature resistan、Filler: Glass fiber reinf、35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 J |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 90 kJ/m² |
| -30°C | ISO179/1eU | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 190 Mpa |
| Bending stress | ISO178 | 280 Mpa | |
| Tensile modulus | ISO527-2 | 11000 Mpa | |
| Flexural modulus | ISO178 | 9900 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 3.2 % |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 24 mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.0 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 5.8 % |
| Shrinkage rate | MD | ISO294-4 | 0.20 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.8 % |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/73G35HSL BK262 |
|---|---|---|---|
| TD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 220 °C | |
| vicat | ISO306/B50 | 215 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 208 °C | |
| melting temperature | ISO11357-3 | 221 °C | |
| MD | ISO11359-2 | 2E-05 cm/cm/°C |