HDPE SM 5508 Chandra Asri Petrochemical
--
Monofilament, tape, rope, thread, mesh fabric, film, laminate
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Chandra Asri Petrochemical/ SM 5508 |
---|---|---|---|
Impact Strength | 20.0µm,吹膜 | ASTM D3420 | 15.7 J/cm |
film | Test Condition | Test Method | Chandra Asri Petrochemical/ SM 5508 |
---|---|---|---|
Elmendorf tear strength | TD:20.0µm | ASTM D1922 | 58.8 kN/m |
Tensile modulus | 20µm,吹塑薄膜,TD | ASTM D882 | 750 MPa |
Dart impact | 20µm,吹塑薄膜 | ASTM D1709 | 50 g |
Tensile modulus | 20µm,吹塑薄膜,MD | ASTM D882 | 600 MPa |
film thickness | 20 µm | ||
Elmendorf tear strength | MD:20.0µm | ASTM D1922 | 11.8 kN/m |
tensile strength | TD:断裂,20µm,吹塑薄膜 | ASTM D882 | 60.0 MPa |
elongation | MD:断裂,20µm,吹塑薄膜 | ASTM D882 | 650 % |
TD:断裂,20µm,吹塑薄膜 | ASTM D882 | 750 % | |
tensile strength | MD:断裂,20µm,吹塑薄膜 | ASTM D882 | 70.0 MPa |
physical property | Test Condition | Test Method | Chandra Asri Petrochemical/ SM 5508 |
---|---|---|---|
density | ASTM D1505 | 0.954 g/cm³ | |
Environmental stress cracking resistance | F50 | ASTM D1693 | 155 hr |
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.75 g/10min |
Thermal performance | Test Condition | Test Method | Chandra Asri Petrochemical/ SM 5508 |
---|---|---|---|
vicat | ASTM D1525 | 129 °C | |
brittle temperature | ASTM D746 | <-70.0 °C |