PA66 HTN 53G50LWSF BK083 DUPONT USA
Zytel®
Food containers
Flame retardant,Thermal stability,High temperature resistan,Glass fiber reinforced,Filler: Glass fiber reinf,50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 95 kJ/m² |
| -30°C | ISO 179/1eU | 65 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 234 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 254 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 5.9E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1.7E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 5.9E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 9.5E-05 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 260 °C |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 16000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| tensile strength | 断裂 | ISO 527-2 | 250 Mpa |
| bending strength | ISO 178 | 390 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| flexural modulus | ISO 178 | 15000 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.20 % |
| flammability | Test Condition | Test Method | DUPONT USA/HTN 53G50LWSF BK083 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |