Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PP Homopolymer WPP PP PRC25TF2HFL-Black Washington Penn Plastic Co. Inc.
--
Applications in the automotive field, automotive external components
Filler, Washington, Penn, Washington, USA, Penn
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PRC25TF2HFL-Black |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
Impact strength of cantilever beam gap | 23°C,6.00mm | ASTM D256 | 32 J/m |
23°C | ISO 180 | 3.5 kJ/m² | |
-10°C | ISO 180 | 2.4 kJ/m² | |
-40°C | ISO 180 | 2.0 kJ/m² | |
-10°C,6.00mm | ASTM D256 | 21 J/m |
hardness | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PRC25TF2HFL-Black |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 94 |
Mechanical properties | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PRC25TF2HFL-Black |
---|---|---|---|
tensile strength | 屈服 | ISO 527-2/5 | 29.0 MPa |
elongation | 断裂 | ASTM D638 | 20 % |
bending strength | 6.00mm | ASTM D790 | 48.0 MPa |
Flexural modulus | 6.00mm | ASTM D790 | 2600 MPa |
Tensile strain | 断裂 | ISO 527-2/5 | 10 % |
tensile strength | 屈服 | ASTM D638 | 31.0 MPa |
Flexural modulus | ISO 178 | 2200 MPa |
physical property | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PRC25TF2HFL-Black |
---|---|---|---|
melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 10 g/10min |
density | ASTM D792 | 1.07 g/cm³ | |
ISO 1183 | 1.07 g/cm³ | ||
melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 10 g/10min |
Thermal performance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PRC25TF2HFL-Black |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 71.0 °C |
0.45MPa,未退火,HDT | ISO 75-2/B | 122 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 73.0 °C | |
0.45MPa,Unannealed,6.00mm,HDT | ASTM D648 | 140 °C |