Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
CPE Macromeric® 0110-108 BK USA Saco Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| Shore hardness | 邵氏D,10秒 | ASTM D2240 | 52 |
| 邵氏A,1秒 | ASTM D2240 | 91 |
| Mechanical properties | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 300 % |
| tensile strength | 断裂 | ASTM D638 | 15.9 MPa |
| Flexural modulus | ASTM D790 | 345 MPa |
| flammability | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 44 % |
| aging | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| Change rate of ultimate elongation in air | 121°C,168hr | ASTM D638 | -15 % |
| 100°C,96hr,在IRM902油中 | ASTM D638 | -25 % | |
| Change rate of tensile strength in air | 75°C,1440hr,在IRM902油中 | ASTM D638 | -20 % |
| Change rate of ultimate elongation in air | 75°C,1440hr,在IRM902油中 | ASTM D638 | -25 % |
| Change rate of tensile strength in air | 121°C,168hr | ASTM D638 | -5.0 % |
| 100°C,96hr,在IRM902油中 | ASTM D638 | -25 % |
| physical property | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 6.0 g/10min |
| density | ASTM D792 | 1.37 g/cm³ |
| elastomer | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| tear strength | 23°C | ASTM D470 | 78.8 kN/m |
| Thermal performance | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0110-108 BK |
|---|---|---|---|
| deformation | 100°C | UL 1277 | 7.0 % |
| brittle temperature | ASTM D746 | -33.0 °C | |
| deformation | 121°C | UL 1277 | 14 % |