PA12/F/PTFE IFL-4036 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/IFL-4036 |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 12 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 73 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 4.27 J | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 17.7 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/IFL-4036 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 3.2 % |
| Flexural modulus | ASTMD790 | 8620 Mpa | |
| Bending stress | ISO178 | 232 Mpa | |
| Dynamic | ASTMD3702Modified | 0.55 | |
| Tensile modulus | ASTMD638 | 9970 Mpa | |
| bending strength | ASTMD790 | 241 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 3.0 % |
| Static | ASTMD3702Modified | 0.51 | |
| Tensile stress | 断裂 | ISO527-2 | 157 Mpa |
| Tensile modulus | ISO527-2/1 | 10300 Mpa | |
| tensile strength | 断裂 | ASTMD638 | 154 Mpa |
| Flexural modulus | ISO178 | 7920 Mpa | |
| Wear factor - Washer | ASTMD3702Modified | 9.00 10^-10in^5-min/ft-lb-hr |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/IFL-4036 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.17 % |
| Shrinkage rate | MD:24小时 | ISO294-4 | 0.24 % |
| TD:24小时 | ISO294-4 | 0.84 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.10 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/IFL-4036 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 201 °C | |
| MD：-40到40°C | ISO11359-2 | 2.6E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7.7E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 198 °C |
| TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |