Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA NILAMID® XS3 GF65 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | kJ/m² | 12 13 |
| -30°C | kJ/m² | 12 -- | |
| Impact strength of cantilever beam gap | 23°C | kJ/m² | 12 13 |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 90 85 |
| -30°C | kJ/m² | 85 -- |
| Mechanical properties | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | % | 2.5 2.8 |
| tensile strength | 屈服,23°C | MPa | 240 225 |
| Tensile modulus | 23°C | MPa | 24000 23500 |
| Electrical performance | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| Volume resistivity | 23°C | ohms·cm | 1E+14 -- |
| Compared to the Leakage Tracking Index (CTI) | 3.20mm,解决方案A | V | PLC 0 |
| dielectric strength | 2.00mm | kV/mm | 32 -- |
| Surface Resistivity | ohms | 1E+13 -- |
| flammability | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | HB -- | |
| 0.8mm | HB -- | ||
| 1.6mm | HB -- | ||
| 0.40mm | HB -- |
| physical property | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| Shrinkage rate | MD:23°C | % | 0.050 -- |
| Water absorption rate | 饱和,23°C | % | 3.4 -- |
| density | 23°C | g/cm³ | 1.79 -- |
| Shrinkage rate | TD:23°C | % | 0.28 -- |
| Water absorption rate | 23°C,24hr | % | 0.40 -- |
| Thermal performance | Test Condition | Test Method | Celanese Corporation/NILAMID® XS3 GF65 |
|---|---|---|---|
| Continuous use temperature | °C | 120 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 235 -- |