PPS A515 TORAY JAPAN
Torelina®
Electrical field,Electronic field,Automotive sector,sporting goods
wear resistant,Flame retardant,Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
BarFlowLength | 320°C,1.00mm | Internal Method | 170 mm |
hardness | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Rockwell hardness | R-Scale | ISO 2039-2 | 120 |
thermal performance | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 260 °C |
Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3.5E-05 cm/cm/°C |
MD | ISO 11359-2 | 2.4E-05 cm/cm/°C | |
Melting temperature | ISO 11357-3 | 278 °C |
mechanical properties | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Bending modulus | 23°C | ISO 178 | 12000 Mpa |
bending strength | 23°C | ISO 178 | 220 Mpa |
Friction coefficient | 0.15 | ||
shear strength | 23°C | JISK7214 | 60.0 Mpa |
Taber abraser | 1000Cycles | ISO 9352 | 50.0 mg |
Tensile strain | Break,23°C | ISO 527-2 | 1.6 % |
tensile strength | Yield,23°C | ISO 527-2 | 145 Mpa |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Dielectric constant | 23°C,1MHz | IEC 60250 | 3.40 |
Dielectric strength | IEC 60243-1 | 26 KV/mm | |
Dissipation factor | 23°C,1MHz | IEC 60250 | 2E-03 |
Volume resistivity | IEC 60093 | 1E+16 ohms·cm |
Physical properties | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Shrinkage rate | TD:3.00mm2 | Internal Method | 0.85 % |
MD:3.00mm4 | Internal Method | 0.20 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
impact performance | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 35 kJ/m² |
flammability | Test Condition | Test Method | TORAY JAPAN/A515 |
---|---|---|---|
UL flame retardant rating | 0.73mm | UL 94 | V-0 |