PA6 GLAMIDE® T-779 TOYOBO CO., LTD.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
Rockwell hardnessASTM D785120 R
Mechanical propertiesTest ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
bending strength23°CASTM D790110 MPa
Impact strength of cantilever beam gap-40°CASTM D25660.0 J/m
tensile strength -40°CASTM D63880.0 MPa
Impact strength of cantilever beam gap23°CASTM D256105 J/m
tensile strength 23°CASTM D63865.0 MPa
bending strength80°CASTM D79048.0 MPa
Flexural modulus23°CASTM D7904000 MPa
80°CASTM D7901100 MPa
-40°CASTM D7905900 MPa
elongation at break23°CASTM D63816 %
Impact strength of cantilever beam gap悬壁梁缺口冲击强度ASTM-D256NB
bending strength-40°CASTM D790140 MPa
tensile strength 80°CASTM D63831.0 MPa
Electrical performanceTest ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
Dissipation Factor体积电阻ASTM D2571E+09 Ω.cm
dielectric strength2.00mmASTM D14921.0 KV/mm
2.00mm，湿态ASTM D14916.0 KV/mm
Volume resistivityASTM D2571E+12 Ω.cm
Dissipation Factor耐电弧性ASTM D495120 s
Flame retardant performanceTest ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
UL flame retardant ratingUL -94HB -
physical property Test ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
Shrinkage rateTD3.00mmASTM D9950.80-1.3 %
densityASTM D7921.43 g/cm³
Water absorption rateASTM D5700.70 %
熔融流动指数10 g/10min
Shrinkage rateMD1.00mmASTM D9950.30-0.50 %
Thermal performanceTest ConditionTest MethodTOYOBO CO., LTD./GLAMIDE® T-779
Linear coefficient of thermal expansionMDASTM D6967.4E-05 cm/cm／°C
Heat distortion temperature1.80MPa未退火，HDTASTM D64896.0 °C
0.45MPa未退火，HDTASTM D648183 °C