PC SABIC INNOVATIVE NANSHA 915AU

Injection grade

US$ 3,530 / MT

FOB Guangzhou port, China

optical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
Refractive index		ISO 489	1.586
transmissivity	2540μm	ASTM D1003	88.0 %
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
bending strength	--5,6	ISO 178	98.0 Mpa
bending strength		Yield,50.0mmSpan4	ASTM D790	95.0 Mpa
--9		ISO 178	98.0 Mpa
crack		ASTM D638	66.0 %
Bending modulus	50.0mmSpan4	ASTM D790	2400 Mpa
--8		ISO 178	2400 Mpa
crack		ISO 527-2/50	66.0 %
elongation	Break	ISO 527-2/50	100 %
50.0mm span		ASTM D790	2400 Mpa
elongation	Yield3	ASTM D638	6.0 %
elongation		Yield	ISO 527-2/50	6.0 %
--2		ASTM D638	2400 Mpa
yield		ISO 527-2/50	66.0 %
elongation	Break3	ASTM D638	100 %
Yield, 50.0mm span		ASTM D790	95.0 Mpa
tensile strength	Break	ISO 527-2/50	66.0 Mpa
yield		ASTM D638	6.0 Mpa
tensile strength	Yield	ISO 527-2/50	66.0 Mpa
tensile strength		Yield3	ASTM D638	66.0 Mpa
Tensile modulus	--2	ASTM D638	2400 Mpa
Tensile modulus		--	ISO 527-2/1	2400 Mpa
Bending modulus	--5	ISO 178	2400 Mpa
tensile strength	Break3	ASTM D638	66.0 Mpa
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
23°C		ISO 180/1A	65 kJ/m²
-30°C		ASTM D256	110 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
-30°C		ISO 179/1eA	12 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	65 kJ/m²
23°C		ASTM D256	650 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J
-30°C		ISO 180/1A	11 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
23°C		ISO 179/1eA	65 kJ/m²
23°C			ISO 179/2C	11 kJ/m²
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
melt mass-flow rate	300°C/1.2kg	ASTM D1238	23 g/10min
Shrinkage rate	MD：--1	Internal Method	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	21.0 cm3/10min
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
1.8MPa, unannealed, 3.20mm		ASTM D648	125 °C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	123 °C
Flow: -40 to 40 ° C		ASTME831	7E-05 cm/cm/°C
Vicat softening temperature	--	ASTMD152510	140 °C
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	134 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	125 °C
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	7E-05 cm/cm/°C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	123 °C
Vicat softening temperature	--	ISO 306/B120	141 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD:-40to40°C	ASTME831	7E-05 cm/cm/°C
flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/915AU
UL flame retardant rating	3.00mm	UL 94	V-0
		1.5mm	UL 94	V-2
		3.0mm	UL 94	V-0
		1.50mm	UL 94	V-2