Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP L304G35 TORAY JAPAN
SIVERAS™
Electrical components、Electrical appliances
enhance、Glass fiber reinforced、High mobility、Filler: Glass fiber reinf、35% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 75 J/m |
| hardness | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 50 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| dielectric constant | ASTM D150 | 4.10 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ASTM D790 | 160 Mpa | |
| Flexural modulus | ASTM D790 | 13000 Mpa | |
| tensile strength | ASTM D638 | 135 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| UL flame retardant rating | 0.200mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.010 % |
| density | ASTM D792 | 1.65 g/cm³ | |
| Shrinkage rate | MD:1.00mm3 | 内部方法 | -0.030 % |
| TD:1.00mm2 | 内部方法 | 0.83 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/L304G35 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 270 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.0E-6to2.5E-5 cm/cm/°C |