Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 PFD04S-BKNAT SABIC INNOVATIVE US
LNP™ STAT-KON™
--
Filler: Glass charcoal po
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 50 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 107 Mpa |
| bending strength | --3 | ISO 178 | 152 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 87.0 Mpa |
| bending strength | --4 | ISO 178 | 136 Mpa |
| Flexural modulus | ISO 178 | 5900 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.6 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+4-1.0E+6 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PFD04S-BKNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 3.5E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 214 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 195 °C | |
| RTI Imp | UL 746 | 65.0 °C | |
| RTI Elec | UL 746 | 65.0 °C |
Contact Us
Get App
Top